| Place of Origin: | China |
|---|---|
| Brand Name: | Homey |
| Model Number: | 680 |
| Minimum Order Quantity: | 9600 Piece/Pieces |
| Price: | $1.07 - $1.12 / Piece |
| Packaging Details: | 280ml;300ml.24PCS/CTN 20' Container 24pcs/ctn,2000 cartons without pallet,1440 cartons with pallet |
| Supply Ability: | 480000 Piece/Pieces per Day |
| CAS No.: | 7085-85-0 | Other Names: | Silicone Sealant |
|---|---|---|---|
| MF: | Mixture | EINECS No.: | 230-391-5 |
| Classification: | Other Adhesives | Main Raw Material: | Silicone |
| Usage: | Construction | Type: | Silicone Sealant |
| HS Code: | 3506100010 | Curing System: | Neutral Cure |
| Component: | One Component | Volume: | 280ml 300ml 310ml |
| Color: | White Black Clear Red Brow | Performance: | Bonding, Sealling |
| OEM: | Avaliable | Price: | Negotiable |
| Shelf Life: | 12 Months | Storage: | Store At 25℃ Or Below |
| Port: | Shenzhen | ||
| High Light: | clear silicone caulk,heat resistant sealant |
||
Homey 680 transparent building acetoxy liquid weatherproof silicone sealant
Homey 680 transparent building acetoxy liquid
weatherproof silicone sealant
INTRODUCTION:
Homey 680 is a one-part, acetoxy cure, high quality, versatile silicone sealant that exhibits outstanding bonding properties. It has excellent weathering resistance, durability, sealing and adhesive properties. For glass and glazing application.
TYPICAL USES:
lSealing glass, glazed ceramics, porcelains vitreous enamels & some non-porous substrates
lTraditional glazing application, e.g.
lGlass sealing & aquariums
|
Test Method |
Test Parameter |
Unit |
Result |
|
As Supplied-Tested at 25℃ and 50% RH
|
|||
|
CTM 101 |
Specific Gravity |
g/ml |
0.98 |
|
ISO |
7390 |
Flow (sag or slump) mm |
0 |
|
ASTM C603 |
Extrusion Rate |
ml/minute |
130 |
|
CTM 001 |
Tack-free |
minute |
≤1 |
|
CTM 003 |
Curing Speed, average |
mm/day |
2 |
|
As Cured-after 14 days at 25℃ and 50% RH |
|||
|
ASTM C661 |
Durometer Hardness, Shore A |
Points |
22 |
|
ISO 9047 |
Movement Capability |
% |
±20 |
|
ISO 8339 |
Tensile/Modulus at,50%Elongation |
Mpa |
0.32 |
|
|
Tensile/Modulus at,100%Elongation |
Mpa |
0.38 |
|
|
Ultimate Tensile Strength |
Mpa |
0.45 |
|
|
Ultimate Elongation at Break |
% |
300 |